6080PN-3-Z high solid resin (special two component liquid)
1.Application : high thickness, for mid layer
2.Product data
Appearance：light yellow transparent sticky liquid
Solvent：DMF
Viscosity (mPa·s/25℃)：8000±2000
Solid content(%)：95士2
100% M.D（kg/cm2）：20
Tensile strength（kg/cm2）：280
Elongation（%）：400
3.Property
①Can be used for long-time production, and the viscosity changes little, thick film coating effect is good.
②Film properties: hydrolysis resistance, heat resistance softening(not suitable for embossing), low temperature property is good
4.Operation
6080PN-3-Z:100
6140G :8
Special pigment: 0-5
6140G is the special curing agent for 6080PN-3-Z, the proportion is 100:8
140℃ Drying for 3 minutes→lamination with 335 base material→130℃drying for 3-5 minutes
5. Notes
1.Adjust the proportion of 6080PN-3-Z and 6140G can influence the speed and strength of getting film
2.6080PN-3-Z ,6140G are high solid products, with low temperature can not flow, please use them at 20-30℃。
3.This product need special non solvent pigment
4.In winter, it is better used in 30℃±5℃. When warming the temperature can not over 60℃，because stir for long time the viscous will be low, and the material will cross link.
5. 300g/m2 coating, the oven temperature usually be 120℃*1min+135℃*1min+145℃*1min. When drying, please keep the volume of air in the oven consistent, to avoid the phenomenon of different curing speed.
Different coating amount should be different mins: 0.25mm should be 3.5mins, 0.15mm should be 3mins, 0.075should be 2.5mins
6.The surface resin we recommend our product 335(one component bottom liquid)
7.This product easy to have bubbles, so it need special defoaming agent. And use the defoaming agent at the beginning of drying time.